Difference between revisions of "Photographs of corrosion and surface defects"
From GlueXWiki
| Line 7: | Line 7: | ||
|width="415pt"|[[Image:l5_02_closeup.jpg|thumb|none|400px|figure 1a: Photograph of 5micron/Left#2 flaw taken 09/08.]] | |width="415pt"|[[Image:l5_02_closeup.jpg|thumb|none|400px|figure 1a: Photograph of 5micron/Left#2 flaw taken 09/08.]] | ||
|width="415pt"|[[Image:l5_02_closeup_new.jpg|thumb|none|400px|figure 1b: Photograph of 5micron/Left#2 flaw taken 03/09.]] | |width="415pt"|[[Image:l5_02_closeup_new.jpg|thumb|none|400px|figure 1b: Photograph of 5micron/Left#2 flaw taken 03/09.]] | ||
| + | |- | ||
| + | |||
| + | |} | ||
| + | |||
| + | Below are before and after photographs for one of the central 2 micron boards. There is evidence for either oxidation of the copper or left-over photo-resist material present upon arrival of the boards from the manufacturer. | ||
| + | |||
| + | {| border="1" cellpadding="2" | ||
| + | |- | ||
| + | |width="415pt"|[[Image:c2_02_closeup.jpg|thumb|none|400px|figure 2a: Photograph of 2micron/Center#2 flaw taken 09/08.]] | ||
| + | |width="415pt"|[[Image:c2_02_closeup_new.jpg|thumb|none|400px|figure 2b: Photograph of 2micron/Center#2 flaw taken 03/09.]] | ||
|- | |- | ||
|} | |} | ||
Revision as of 16:59, 27 March 2009
Photographs of flaws in the Allflex films were taken when the boards arrived in September '08 and again in March '09 after being stored in a dry Nitrogen environment. The first two photographs below show that there was already evidence for corrosion or poor quality of the copper surface on one of the 5 micron boards when they arrived from the manufacturer, but it is not clear that this problem became worse over time.
Below are before and after photographs for one of the central 2 micron boards. There is evidence for either oxidation of the copper or left-over photo-resist material present upon arrival of the boards from the manufacturer.